Ti-Al基合金化合物的制备
Preparation of Ti-Al-based Compound
王海东
点击:3122次 下载:0次
作者单位:长春工程学院 机电学院, 吉林 长春 130012
中文关键字:Ti-Al基金属间化合物; 球磨时间; 组织形貌
英文关键字:Ti-Al intermetallic compound; milling time; microstructure
中文摘要:以50at%Al、50at%Ti配比的混合粉末为原料,采用三维摆动式高能球磨机在Ar气保护下对混合粉末分别进行球磨5、10、15和20 h。并利用X射线仪、扫描电镜、透射电镜及能谱仪对球磨后的Ti-Al基金属间化合物进行组织形貌、显微结构及成分分析。分析结果表明,20 h球磨时间为最佳。
英文摘要:The mixed powder with 50at%Al and 50at%Ti were milled by three-dimensional swing-style high energy ball mill machine in Ar gas, and the milling time is respectively 5 h, 10 h, 15 h and 20 h. The morphology, microstructure and composition of TiAl intermetallic compound were studied by X-ray,SEM, TEM and EDS. The results show that milling for 20 h is best.