退火温度对ZL102组织和性能的影响
Effect of Annealing Temperature on Microstructure and Properties of ZL102 Alloy
赵爱彬, 张莹莹, 王运玲
点击:3285次 下载:0次
作者单位:辽宁石油化工大学 材料工程系, 辽宁 抚顺 113001
中文关键字:ZL102铝合金; 退火; 显微组织; 耐蚀性
英文关键字:ZL102; anneal; microstructure; corrosion resistance
中文摘要:利用金相显微镜观察经不同温度退火处理的ZL102合金的显微组织,通过测量硬度得出其随退火温度的变化规律;并通过全浸腐蚀试验比较其耐腐蚀性,观察其在不同温度下的腐蚀形貌。结果表明,经不同温度退火处理的材料其显微组织发生明显的改变,硬度随退火温度呈一个波动趋势;在250 ℃和300 ℃退火处理时其腐蚀形貌较好。
英文摘要:The microstructure of ZL102 alloy was observed after annealing at different temperature by metallography microscope. The rule of hardness changing along with annealing temperature was obtained, the corrosion resistance was compared by all soaks, the corrosion appearance was observed. The results show that the microstructure has obvious change throngh annealing at different temperature, hardness assumes a fluctuation tendency along with the annealing temperature. The corrosion morphology is good at 250 ℃ and 300 ℃.