含钒双相钢临界区热处理温度的研究
Research on Critical Heat Treatment Temperature of Dual-phase Steel with Vanadium
田志强, 唐 荻, 江海涛, 孙婷婷
点击:3454次 下载:0次
作者单位:(北京科技大学 高效轧制国家工程研究中心, 北京 100083)
中文关键字:双相钢; 临界区; 钒
英文关键字:dual-phase steel; intercritical zone; vanadium
中文摘要:采用扫描和透射电镜对模拟连续退火处理的试样进行分析,对含钒双相钢临界区的热处理温度和钢中钒的存在状态进行了研究。结果表明,在其他工艺条件相同时,随临界区热处理温度升高,双相钢的强度降低。双相钢中的钒主要以两种状态存在,一种是以析出物的状态存在,一种是在马氏体中以固溶状态存在,双相钢中的钒起到析出强化、细化晶粒和提高淬透性的作用。
英文摘要:The effects of intercritical heat treat temperature on properties and vanadium distribution of dual-phase steel with vanadium were studied by SEM and TEM. The results show that the strength reduces with intercritical annealing temperature going up, while other process condition is same. Vanadium has two kinds of existent states, one is precipitate in ferrite, another one is solute in martensite, the main roles of vanadium in dual-phase steel is precipitation strength, refining grain size and rising hardenability.