Mg含量对Al-5%Cu合金凝固组织细化作用的研究
Effects of Mg on Solidification Structure Refinement of Al-5%Cu Alloy
何力佳，王建中，王春波，曹丽云
点击：3528次 下载：0次
作者单位：（辽宁工业大学 材料与化学工程学院，辽宁 锦州 121001）
中文关键字： 铝铜合金；凝固组织；细化
英文关键字：Al-Cu alloy； solidification structure; refinement
中文摘要：系统地研究了不同Mg含量对Al-5%Cu合金凝固组织及性能的影响。结果表明：Mg元素对Al-5%Cu合金晶粒有细化作用，当Mg含量(质量分数)为0.8%时，细化效果较好，晶粒尺寸为0.912 mm，二次枝晶间距为42.9 μm，显微硬度值为74.16HV0.025，在磨损实验中合金失重较少，即抗磨损能力较强。
英文摘要：To improve the property of Al-5%Cu alloy, the effects of Mg element on Al-5%Cu alloy solidification structure were studied. The results show that Mg has refinement on the solidification structure of Al-5%Cu alloy and can increase the matrix microhardness and anti-wear property, when the Mg content is 0.8%, the grain refinement is better relatively, the grain size is 0.912 mm, the secondary dendrite space is 42.9 μm， the matrix microhardness is 74.16HV0.025.