SWRH82B钢奥氏体动态再结晶的实验研究
Experimental Study on Dynamic Recrystallizatuon of Austenite SWRH82B Steel
蒋 煦, 卫广智, 齐福利
点击:3235次 下载:0次
作者单位:贵州大学 材料与冶金学院, 贵州 贵阳 550003
中文关键字:动态再结晶; 变形温度; 应变速率; 临界变形量; 参数Z
英文关键字:dynamic recrystallization; deformation temperature; strain rate; critical deformation; parameter Z
中文摘要:以线材SWRH82B为研究对象,采用GLEEBLI-2000热模拟试验机对奥氏体动态再结晶进行实验研究。通过实测数据,分析了变形温度、变形速率对动态再结晶的影响;同时,分析了参数Z和动态再结晶的关系。结果表明:升高变形温度、降低变形速率,Z值越小,容易促进动态再结晶发生。
英文摘要:An experimental study of dynamic recrystallizatuon of austenite SWRH82B steel was carried out using Gleeble-2000 thermal simulator. The effects of deformation temperature and deformation rates on the dynamic recryatallization process were studied by the experimental datas. The relation between dynamic recrystallization of austenite SWRH82B steel and parameter Z was analyzed. The results show that the dynamic recystallization occurs when deforming at high-temperature, low-deformation rate and low parameter Z.