残余奥氏体对滚动轴承疲劳寿命的影响
Influence of Retained Austenite on Fatigue Life of Rolling Bearing
钱 坤
点击:3223次 下载:0次
作者单位:(杭州职业技术学院, 浙江 杭州 310018)
中文关键字:滚动轴承; 热处理工艺; 残余奥氏体; 疲劳寿命
英文关键字:rolling bearing; heat treatment process; retained austenite; fatigue life
中文摘要:分析滚动轴承表面疲劳剥落失效机理和残余奥氏体对疲劳寿命的影响,确定控制残余奥氏体含量的热处理工艺,进行残奥量测试与轴承疲劳寿命试验。结果表明,残余奥氏体含量为12%时,轴承的疲劳寿命较高。
英文摘要:The fatigue spalling failure mechanism of rolling bearing surface and the influences of retained austenite content on the worklife of bearing fatigue spalling were analyzed. The heat treatment process for controling the retained austenite was content determined. The tests on the retained austenite content and bearing fatigue life were carried out. The results show that the worklife of the rolling bearing is longer when retained austenite content 12%.