管材内高压成形产品失效机理分析及对策研究
Failure Mechanism Analysis and Measure Research on Tube Internal High-pressure Forming
陈 维1, 庄千芳1,2
点击:3681次 下载:0次
作者单位:1.浙江工贸职业技术学院 汽车教研室,浙江 温州325003; 2.浙江万强法兰有限公司,浙江 温州325024
中文关键字:内高压成形;缺陷机理;成形工艺
英文关键字: internal high-pressure forming; failure mechanism; forming process
中文摘要:通过管材对内高压成形过程中产生的起皱、折叠、屈曲和破裂等这几种常见缺陷机理进行深入分析研究,找出了失效原因,提出了较为可行的解决方案,对内高压成形的产品具有实际指导意义。
英文摘要:The failure mechanisms of some common defects, such as wrinkle, fold, bend and crack in tube internal high-pressure forming process were studied to find the reasons of failure. The feasible schemes were put forward, which had practical guiding significance in tube internal high-pressure forming process.