热处理对TiAlCeN涂层结构和性能的影响
Effect of Heat Treatment on Microstructure and Performance of TiAlCeN Coating
陈一胜, 张雪辉, 陈 颢, 刘海浪
点击:2905次 下载:0次
作者单位:(江西理工大学 材料与化学工程学院, 江西 赣州 341000)
中文关键字:TiAlCeN涂层; 电弧离子镀; 热处理; 显微硬度
英文关键字:TiAlCeN coating; arc ion plating; heat treatment; microhardness
中文摘要:采用电弧离子镀(AIP)技术制备了TiAlCeN涂层,并对其进行800~1100 ℃热处理。采用SEM、显微硬度仪和划痕试验机等研究了不同温度和保温时间下涂层微观结构和性能的变化。结果表明:经900 ℃× 3 h高温处理后的TiAlCeN涂层刀片综合性能最优,其显微硬度可达2000 HV0.5,结合强度最高可达65 N。
英文摘要:The TiAlCeN coating prepared by arc ion plating was heat-treated at 800 ℃~1100℃. The changes of microstructure and properties of the coating treated at different temperature for different time were examined by SEM, microhardness test and scratch test . The results show that heat treatment at 900 ℃for 3 h is the best heat treatment. Its microhardness is up to 2000 HV0.5 and the bonding strength is up to 65 N.