ZG0Cr13Ni4Mo铸造导叶孔洞缺陷的研究
Study on Porosity Defect of ZG0Cr13Ni4Mo Guide Vane Casting
匡 毅1, 沈仁坤2, 郭立辉1
点击:2742次 下载:0次
作者单位:1. 郑州机械研究所, 河南 郑州 450001; 2. 重庆云河水电股份有限公司, 重庆 400050
中文关键字:导叶;孔洞缺陷;分散缩孔;气孔
英文关键字: guide vane; porosity defect; dispersed shrinkage; gas-hole defect
中文摘要:对ZG0Cr13Ni4Mo铸造导叶热节附近出现的孔洞缺陷进行分析,结果表明,此类孔洞不是分散缩孔,而是内生式N2与CO复合型气孔缺陷。进而对此类缺陷提出相关防范措施。
英文摘要:The forming cause of porosity defect nearby hot spot of ZG0Cr13Ni4Mo guide vane casting was analyzed. The results show that the porosity is not dispersed shrinkage, but gas-hole caused by N2 and CO. Then responding measures availably solving gas-hole defect of the casting are put forward by practical production.